Faculty Bibliography

PURPOSE: To investigate the influence of atmospheric pressure plasma (APP) treatment on the microtensile dentin bond strength of two etch-and-rinse adhesive systems, after one week and one year of water storage, and additionally to observe the micromorphology of resin/dentin interfaces under scanning electronic microscopy (SEM). MATERIALS AND METHODS: The occlusal enamel was removed from third human molars to expose a flat dentin surface. The teeth were then randomly divided into six groups (n = 7), according to two adhesives (Optibond FL and XP-Bond) and three APP treatments (untreated dentin [control], APP application before or after acid etching). After performing the composite resin buildup on bonded dentin, the teeth were sectioned perpendicularly to the bonded interface to obtain beam-shaped specimens (cross-sectional area of ~0.9 mm2). The specimens were tested in tension until failure after one week and one year of water storage (1.0 mm/min rate). Bond strength data were analyzed by three-way ANOVA and Tukey's post-hoc test (alpha = 0.05%). Bonded beam specimens from each tooth were also prepared for interfacial SEM investigation. RESULTS: At one week, APP treatment applied after acid etching increased the dentin bond strength for XP Bond, while no effect was observed for Optibond FL. After one year, the bond strength of XP Bond decreased in groups where APP was applied after etching. The evaluation time did not influence the bond strength for Optibond FL. CONCLUSION: One-year evaluation did not show any sign of degradation of interfacial structures in any group. Application of APP to etched dentin combined with a two-step etch-and-rinse adhesive significantly increased bond strength at one week, but the effect was not stable after one year and was adhesive dependent.

A bone drilling concept, namely osseodensification, has been introduced for the placement of endosteal implants to increase primary stability through densification of the osteotomy walls. This study investigated the effect of osseodensification on the initial stability and early osseointegration of conical and parallel walled endosteal implants in low density bone. Five male sheep were used. Three implants were inserted in the ilium, bilaterally, totaling 30 implants (n=15 conical, and n=15 parallel). Each animal received 3 implants of each type, inserted into bone sites prepared as follows: (i) regular-drilling (R: 2mm pilot, 3.2mm, and 3.8mm twist drills), (ii) clockwise osseodensification (CW), and (iii) counterclockwise (CCW) osseodensification drilling with Densah Bur (Versah, Jackson, MI, USA): 2.0mm pilot, 2.8mm, and 3.8mm multi-fluted burs. Insertion torque as a function of implant type and drilling technique, revealed higher values for osseodensification relative to R-drilling, regardless of implant macrogeometry. A significantly higher bone-to-implant contact (BIC) for both osseodensification techniques (p<0.05) was observed compared to R-drilling. There was no statistical difference in BIC as a function of implant type (p=0.58), nor in bone-area-fraction occupancy (BAFO) as a function of drilling technique (p=0.22), but there were higher levels of BAFO for parallel than conic implants (p=0.001). Six weeks after surgery, new bone formation along with remodeling sites was observed for all groups. Bone chips in proximity with the implants were seldom observed in the R-drilling group, but commonly observed in the CW, and more frequently under the CCW osseodensification technique. In low-density bone, endosteal implants present higher insertion torque levels when placed in osseodensification drilling sites, with no osseointegration impairment compared to standard subtractive drilling methods.

PURPOSE: To compare the bone bonding capabilities of 2 different surface treatments at an early healing period. Titanium alloy (Ti6Al4V) custom-made rectangular plates (1.4 x 2.4 x 4 mm) were either dual acid etched (Ti6Al4V-DAE) or DAE/nanotextured blasted (Ti6Al4V-NTB). MATERIALS AND METHODS: Implants were placed in the distal femurs of 10 Wistar rats and were allowed to heal for 9 days. After euthanasia, the bone immediately proximal and distal to the implant was removed to test the bone bonding force with a universal testing machine. Ultrastructure of the bone/implant interface was assessed by scanning electron microscopy. RESULTS: Ti6Al4V-NTB samples exhibited significantly greater bond strength than Ti6Al4V-DAE samples. Morphologically, the Ti6Al4V-NTB surfaces presented intimate interaction with bone, whereas little interaction between the Ti6Al4V-DAE surface and bone was observed. CONCLUSION: The results of this study indicated a significant increase in bone bonding for the DAE/nanotextured blasted surface, which is suggested to be the outcome of the nanotexturing.

The human vocal folds are complex structures made up of distinct layers that vary in cellular and extracellular composition. The mechanical properties of vocal fold tissue are fundamental to the study of both the acoustics and biomechanics of voice production. To date, quantitative methods have been applied to characterize the vocal fold tissue in both normal and pathologic conditions. This review describes, summarizes, and discusses the most commonly employed methods for vocal fold biomechanical testing. Force-elongation, torsional parallel plate rheometry, simple-shear parallel plate rheometry, linear skin rheometry, and indentation are the most frequently employed biomechanical tests for vocal fold tissues and each provide material properties data that can be used to compare native tissue to diseased or treated tissue. Force-elongation testing is clinically useful, as it allows for functional unit testing, while rheometry provides physiologically relevant shear data, and nanoindentation permits micrometer scale testing across different areas of the vocal fold as well as whole organ testing. Thoughtful selection of the testing technique during experimental design to evaluate a hypothesis is critical to optimize biomechanical testing of vocal fold tissues.

The objective of this split-mouth clinical study was to compare a combination of in-office and at-home dental bleaching with at-home bleaching alone. Two applications of in-office bleaching were performed, with one appointment per week, using 38% hydrogen peroxide. At-home bleaching was performed with or without in-office bleaching using 10% carbamide peroxide in a custom-made tray every night for 2 weeks. The factor studied was the bleaching technique on two levels: Technique 1 (in-office bleaching combined with home bleaching) and Technique 2 (home bleaching only). The response variables were color change, dental sensitivity, morphology, and surface roughness. The maxillary right and left hemiarches of the participants were submitted to in-office placebo treatment and in-office bleaching, respectively (Phase 1), and at-home bleaching (Phase 2) treatment was performed on both hemiarches, characterizing a split-mouth design. Enamel surface changes and roughness were analyzed with scanning electron microscopy and optical interferometry using epoxy replicas. No statistically significant differences were observed between the bleaching techniques for either the visual or the digital analyses. There was a significant difference in dental sensitivity when both dental bleaching techniques were used, with in-office bleaching producing the highest levels of dental sensitivity after the baseline. Microscopic analysis of the morphology and roughness of the enamel surface showed no significant changes between the bleaching techniques. The two techniques produced similar results in color change, and the combination technique produced the highest levels of sensitivity. Neither technique promoted changes in morphology or surface roughness of enamel.

PURPOSE: To investigate the probability of survival of different implant-abutment connection designs in narrow versus standard-diameter implants supporting anterior crowns. MATERIALS AND METHODS: A total of 108 implants of either 3.5-mm or 4.0-mm diameter (narrow and standard, respectively) (10 mm in length, Implacil de Bortoli) were divided into six groups (n = 18 each) as follows: external hexagon 3.5 mm or 4.0 mm (EH3.5 or EH4.0), internal hexagon 3.5 mm or 4.0 mm (IH3.5 or IH4.0), and Morse taper 3.5 mm or 4.0 mm (MT3.5 or MT4.0). The corresponding abutments were screwed to the implants, and standardized maxillary central incisor metal crowns were cemented and subjected to step-stress accelerated life testing in water. Use-level probability Weibull curves and reliability for a mission of 50,000 and 100,000 cycles at 100 N and 150 N (90% 2-sided confidence intervals [CI]) were calculated. Polarized-light and scanning electron microscopes were used to assess the failure modes. RESULTS: The calculated reliability with 90% CI for a mission of 50,000 cycles at 100 N and 150 N showed that cumulative damage from the respective loads would lead to ~93% and ~18% implant-supported restoration survival in group EH3.5, ~99% and ~1% in group IH3.5, ~97% and ~89% in the MT3.5, ~100% and ~99% in the group EH4.0, ~100% and ~100% in group IH4.0, and ~99% and ~99% in group MT4.0. For the 100,000-cycle mission, the probability of survival estimated at 100 N and 150 N was, respectively: 0% for EH3.5 and IH3.5 at both load levels, ~96% and ~87% for the MT3.5, 100% and ~99% for EH4.0, 100% and ~99% for IH4.0, and 98% and ~92% for the MT4.0. CONCLUSION: A significant decrease in the probability of survival as a function of elapsed fatigue cycles and load increase was observed for narrow implants only with EH and IH implant-abutment connections, but not on Morse taper.

The degree of interplay among variables in dental implant treatment presents a challenge to randomized clinical trials attempting to answer questions in a timely, unbiased, and economically feasible fashion. Further adding complexity to the different scenarios is the varied implant designs and related bone response, area of implantation, implant bulk material, restoration, abutments and related screws, fixation mode (screwed, fixed, or a combination), and horizontal implant-abutment matching geometry. This article critically appraises the most common mechanical testing methods used to characterize the implant-prostheses complex. It attempts to provide insight into the process of construction of an informed database of clinically relevant questions regarding preclinical evaluation of implant biomechanics and failure mechanisms. The use of single load to failure, fatigue life, fatigue limit, and step-stress accelerated life testing is discussed with emphasis on their deliverables, weaknesses, and strengths. Fractographic analysis and challenges in the correlation between laboratory- and in-service-produced failures of dental ceramics, resin composites, and titanium are introduced. In addition, examples are presented of mechanical characterization studies used in our laboratory to assess some implant-supported rehabilitation variables.

OBJECTIVES: The aim of the study was to analyze the effects of ovariectomy on periodontal tissues following immediate tooth replantation by histomorphometric, immunohistochemistry, and muCT analysis. MATERIALS AND METHODS: Eighty wistar rats (Rattus norvegicus albinos) with normal estrous cycles were randomly divided into two groups: ovariectomized (OVX) and Sham. Two months after surgery, the rats' upper right incisor was extracted followed by immediate reimplantation. The animals were sacrificed after 28, 45, and 60days healing time. Histomorphometric and immunohistochemical analysis were performed by evaluation of PCNA and TRAP straining. RESULTS: The periodontal ligament was reinserted into the bone and cementum in the both groups. The immunohistochemical analysis revealed PCNA positive cells on the periodontal ligament in both groups at 28 days. Root resorption was noted at 45days with immunoreactive cells for TRAP present in bone and tooth surface however no statistical differences between the groups were noticed. Histomorphometric analysis showed significant difference between groups in the periodontal ligament and root resorption parameters for the sub-items: intensity of chronic inflammatory infiltrate at 60days (p<0.01), the organization of the periodontal ligament at 28days (p<0.05), depth of root resorption at 45days (p<0.05) and at 60days (p<0.001). The muCT analysis showed multiple areas of bone resorption in association with OVX at 28 and 60days with no significant differences between times in vivo. CONCLUSION: The ovariectomy did not have significant influence in periodontal tissue parameters following tooth reimplantation.

This study evaluated the effect of microrobotized blasting of titanium endosteal implants relative to their manually blasted counterparts. Two different implant systems were utilized presenting two different implant surfaces. Control surfaces (Manual) were fabricated by manually grit blasting the implant surfaces while experimental surfaces (Microblasted) were fabricated through a microrobotized system that provided a one pass grit blasting routine. Both surfaces were created with the same ~50microm average particle size alumina powder at ~310KPa. Surfaces were then etched with 37% HCl for 20min, washed, and packaged through standard industry procedures. The surfaces were characterized through scanning electron microscopy (SEM) and optical interferometry, and were then placed in a beagle dog radius model remaining in vivo for 3 and 6 weeks. The implant removal torque was recorded and statistical analysis evaluated implant system and surface type torque levels as a function of time in vivo. Histologic sections were qualitatively evaluated for tissue response. Electron microscopy depicted textured surfaces for both manual and microblasted surfaces. Optical interferometry showed significantly higher Sa, Sq, values for the microblasted surface and no significant difference for Sds and Sdr values between surfaces. In vivo results depicted that statistically significant gains in biomechanical fixation were obtained for both implant systems tested at 6 weeks in vivo, while only one system presented significant biomechanical gain at 3 weeks. Histologic sections showed qualitative higher amounts of new bone forming around microblasted implants relative to the manually blasted group. Microrobotized blasting resulted in higher biomechanical fixation of endosteal dental implants and should be considered as an alternative for impant surface manufacturing.

OBJECTIVES: Narrow implants are indicated in areas of limited bone width or when grafting is nonviable. However, the reduction of implant diameter may compromise their performance. This study evaluated the reliability of several narrow implant systems under fatigue, after restored with single-unit crowns. MATERIALS AND METHODS: Narrow implant systems were divided (n = 18 each), as follows: Astra (ASC); BioHorizons (BSC); Straumann Roxolid (SNC), Intra-Lock (IMC), and Intra-Lock one-piece abutment (ILO). Maxillary central incisor crowns were cemented and subjected to step-stress accelerated life testing in water. Use level probability Weibull curves and reliability for a mission of 100,000 cycles at 130- and 180-N loads (90 % two-sided confidence intervals) were calculated. Scanning electron microscopy was used for fractography. RESULTS: Reliability for 100,000 cycles at 130 N was approximately 99 % in group ASC, approximately 99 % in BSC, approximately 96 % in SNC, approximately 99 % in IMC, and approximately 100 % in ILO. At 180 N, reliability of approximately 34 % resulted for the ASC group, approximately 91 % for BSC, approximately 53 % for SNC, approximately 70 % for IMC, and approximately 99 % for ILO. Abutment screw fracture was the main failure mode for all groups. CONCLUSIONS: Reliability was not different between systems for 100,000 cycles at the 130-N load. A significant decrease was observed at the 180-N load for ASC, SNC, and IMC, whereas it was maintained for BSC and ILO. CLINICAL RELEVANCE: The investigated narrow implants presented mechanical performance under fatigue that suggests their safe use as single crowns in the anterior region.